MODELING MICROSTRUCTURAL STRESSES IN POLYMER-SILICATE NANOCOMPOSITE WITH THE INFLUENCE OF SPHERULITIC STRUCTURES
Аннотация:
Polymer nanocomposites based on polyolefins and layered clay minerals (smectites) are multi-layered structure. Even unfilled polyolefins (polyethylene, polypropylene, etc.) are structurally heterogeneous environment consist- ing of amorphous and crystalline phases. Adding filler further complicates the structure of the material. The results of computer simulation of interaction of silicate inclusions, crystalline supermolecular formations in the matrix (spherulites) and its amorphous part. Composite is modeled as a square periodicity cell with inclusion and spherulites. Inclusion was a pack of silica plates separated by thin layers of polymer. Spherulite modeled as “snowflakes” of crystallized lamellae (band areas with an ordered arrangement of polymer molecules). Problem was solved by finite element method in nonlinear-elastic formulation (plane strain).
Ключевые слова:
Постоянный URL
Статьи в номере
- WKB-BASED SCHEMES FOR TWO-BAND SCHR¨ODINGER EQUATIONS IN THE HIGHLY OSCILLATORY REGIME
- COULOMB EFFECTS ON THE SPIN POLARIZATION OF QUANTUM RINGS
- MECHANICAL PROPERTIES OF POLYMER NANOCOMPOSITES BASED ON STYRENE BUTADIENE RUBBER WITH DIFFERENT TYPES OF FILLERS
- PLANAR FLOWS IN NANOSCALE REGIONS
- THE FEATURES OF STRUCTURE TRANSFORMATION CAUSED BY NANO-BURNISHING PROCESS
- INFLUENCE OF SHEAR STRAIN ON STABILITY OF 2D TRIANGULAR LATTICE
- NONLINEAR DYNAMIC VARIATIONS IN INTERNAL STRUCTURE OF A COMPLEX LATTICE
- МОЛЕКУЛЯРНО-ДИНАМИЧЕСКИЙ РАСЧЕТ КОЭФФИЦИЕНТА ТЕПЛОВОГО РАСШИРЕНИЯ НАНОКЛАСТЕРОВ МЕДИ
- МОДЕЛИРОВАНИЕ SiC ФАЗ НА ОСНОВЕ НАНОСТРУКТУР
- О ПРЕДЕЛЬНОЙ ТОЛЩИНЕ ПЕРОВСКИТОПОДОБНОГО БЛОКА В ФАЗАХ АУРИВИЛЛИУСА В СИСТЕМЕ Bi2O3-Fe2O3-TiO2
- СИНТЕЗ И ФИЗИКО-ХИМИЧЕСКИЕ СВОЙСТВА ЛИТИРОВАННЫХ НАНОВИСКЕРОВ НА ОСНОВЕ ОКСИДОВ ВАНАДИЯ
- СИНТЕЗ ВОДНЫХ ЗОЛЕЙ НАНОКРИСТАЛЛИЧЕСКОГО ДИОКСИДА ЦЕРИЯ, ДОПИРОВАННОГО ГАДОЛИНИЕМ
- ИНФОРМАЦИЯ И СТРУКТУРА: МОДУЛЯРНЫЙ ДИЗАЙН ДВУМЕРНЫХ НАНОСТРУКТУР И ФРАКТАЛЬНЫХ РЕШЕТОК